Maxflux SAF-4 is an agglomerated basic type flux having very good performance with good sub-zero impact properties & extreme resistance to cracking. It is neutral in terms of silicon and manganese pick-up. Slag is easily removable and bead finish is smooth & shiny. The diffusible hydrogen content of the weld metal is low.
Maxflux SAF-4 is suitable for single & multi-layer welding of structural steels,
pressure vessels, boilers and other fabrications involving medium tensile & low
alloy steel.
WITH SAW WIRE | Elements | C | Mn | Si | S | P | Cu | |
AUTOTHERME GRADE-A |
| 0.050 | 0.600 | 0.300 | 0.028 | 0.027 | 0.150 | |
AUTOTHERME GRADE-B | Typical | 0.060 | 1.000 | 0.350 | 0.028 | 0.026 | 0.150 | |
AUTOTHERME GRADE-C | Typical | 0.060 | 1.500 | 0.380 | 0.028 | 0.027 | 0.150 |
WITH SAW WIRE | UTS | 0.2% YS | % EI | CVN Impact (Joules) | CVN Impact (Joules) | CVN Impact (Joules) |
(Mpa) | (Mpa) | (L=4d) | -18°C | -29°C | -40°C | |
AUTOTHERME GRADE-A | 460 | 380 | 26 | 40 | 30 | - |
AUTOTHERME GRADE-B | 510 | 415 | 25 | 70 | 60 | 34 |
AUTOTHERME GRADE-C | 530 | 418 | 26 | 90 | 75 | 45 |
SiO2 + TiO2 | CaO+MgO | Al2O3+MnO | CaF2 |
20% | 25% | 20% | 35% |
F8A8/P8-ENI3-NI3, F11A8/F10A4EM4-M4, F9A4/F9P0-EF3-F3, F7A8/P8ENI1-NI1, F8A6ENI2-NI2
F7A2-EL8, F7A4/A5-EM12K,F7A4/P4-EH14, F8A2-EA2-A2
F7A4EH-14, F7A4EM-12K, F8A2EA2-A2
F7A4-EM12K, F7A4/ P4-EH14, F7A4/ P4-EH10K
F7AZ-EL8, F7A0-EM12K
F8A5-EH10K
F8A2-EG-G
F8P2-EB2-B2, F9P2-EB3-B3
F8P2-EB6-B6, F8P2-EB2R-B2, F9P2-EB3R-B3, F9PZ-EB9-B9
F8P2-EA4-A4, F8A4/F7P4-EA3-A3
F7A6/P6/P8-EH10K, F7A8/P8-EH10K
F8A4/ P4-EA2-A2 & EA3-A3, F9A4/ P2-EF3-F3,F11A4/ F10P5-EN4-N4
F7P5/P6-EH10K,F7P5/P6-EH14, F7P6/P8-EH12K
F7AZ-EL8, F7A0-EM12K
F7AZEL-8, F7A0EM-12K
F7A0-EL8, F7A0-EM12K
F7A4/P4-EM12K, F8A4/F7P5-EH14
F7A4-EM12K, F7A5-EH14, F7A5-EH10K
F7A2/P2-EM12K F7A6/P6/P8-EH10K
F7A5-EL8
F8A5/A6-ENi2-Ni2, F8A5/A6-ECNi2-Ni2
F7A5-EH14, F7A5-EM12K, F8A4-EA2-A2
F8P2-EB2/ EB2R-H8
F8P2-EA4-A4
F7A4/ P4-EH14, F7A5/ P5-EH10K