Weld metal having strict control on S, P, As, Sn & Sb will improve the subzero impact property and resists temper embrittlement. Weld metal retains its mechanical properties after prolonged heat treatments. Ideal for welding steam generating equipments and reactor vessels. The weld metal displays excellent tensile strength and creep resistance. Specially applicable wherever temper embrittlement resistance is required.
Element | C | Mn | Si | Cr | Mo | Sb | As | S | P | Sn | Cu | Ni | Ti | V |
Percent | 0.06 | 0.60 | 0.25 | 1.30 | 0.55 | 0.001 | 0.0035 | 0.009 | 0.009 | 0.003 | 0.018 | 0.14 | 0.002 | 0.008 |
|
YS |
UTS |
Elongation |
CVN Impact Strength (J) |
Hardness |
(MPa) |
(MPa) |
(L= 5d)% |
at Minus 33°C |
(VPN) | |
SR at 690°C/ 1 hr |
500 |
580 |
24 |
- |
- |
SR at 690°C/ 2.5 hrs |
450 |
540 |
28 |
150 |
200 |
SR at 690°C/ 16 hrs |
390 |
520 |
30 |
170 |
- |
DIFFUSIBLE HYDROGEN CONTENT: 4 ml/100 gms of weld metal (max.).
X-FACTOR : (10P + 5Sb + 4Sn + As)/100 ≤ 12.0 (Elements in ppm)
4 J-FACTOR: (Si + Mn) x (P + Sn) 10^4 ≤ 125
STEP COOLING REQUIREMENT: CvTr40 +2.5 Δ CvTr40Sc < 10°C (Where CvTr40: Transition temperature at absorbed energy of 40J of heat treated specimen. Δ CvTr40Sc: Shift in 40J transition temperature due to step cooling)
Size (mm) Dia x Length | 6.3x450 | 5x450 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 250-300 | 200-250 | 140-180 | 100-130 | 70-100 |
Qty. (Pcs./Carton) | 25 | 35 | 55 | 75 | 100 |
E8018-B8
E8018-B3L
E8018-B1
E8018-B6
E8018-B8L
E9015-B24
E9018-G
E7018-B2L
E8018-D3
E8018-B8
E8018-G
E8018-D3
E9015-B23
E7018-A1
E9018-B3
E8018-B3L
E8018-B8L
E9018-B3
E9015-B3
E7018-B2L
E8018-B2 H4R
E7018-A1
E8018-B8
E8018-B2
E9015-B91
E7018-A1 H4R
E8018-B6
E9018-B91
E8018-B2
E9018-D1
E9018-G
E8015-B6
E9015-B92
E9016-B3
E9018-B3
E8018-B6L
E9015-B92