Weld metal having lesser impurities i.e. S, P, will improve the subzero impact property and retains its mechanical properties after prolonged heat treatments. Ideal for welding similar composition materials. The weld metal displays excellent tensile strength and creep resistance. Specially applicable wherever the impact o property requirement at subzero temperatures up to minus 20 C.
Element | C | Mn | Si | S | P | Cr | Mo | Sn | As | Sb |
Percent | 0.06 | 0.76 | 0.49 | 0.007 | 0.010 | 1.25 | 0.50 | 0.002 | 0.004 | 0.002 |
UTS | YS | Elongation | CVN Impact Strength (J) | CVN Impact Strength (J) | Creep Strength at 550°C |
(MPa) | (MPa) | (L= 5d)% | at Minus -20°C | 20°C | (1%offset in 10,000 hrs) |
620 | 530 | 22 | 80 | 100 | 120 MPa |
DIFFUSIBLE HYDROGEN CONTENT: 5 ml/100 gms of weld metal (max.).
Size (mm) | 6.3x450 | 5x450 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 250-300 | 200-250 | 140-180 | 100-130 | 70-100 |
Qty. (Pcs./Carton) | 25 | 30 | 50 | 75 | 100 |
E8018-B8
E8018-B3L
E8018-B1
E8018-B6
E8018-B8L
E9015-B24
E9018-G
E7018-B2L
E8018-D3
E8018-B8
E8018-G
E8018-D3
E9015-B23
E7018-A1
E9018-B3
E8018-B3L
E8018-B8L
E9018-B3
E9015-B3
E7018-B2L
E8018-B2 H4R
E7018-A1
E8018-B8
E9015-B91
E7018-A1 H4R
E8018-B6
E9018-B91
E8018-B2
E9018-D1
E9018-G
E8015-B6
E9015-B92
E9016-B3
E8018-B2
E9018-B3
E8018-B6L
E9015-B92