Low carbon, low hydrogen, iron powder electrode depositing 2.25Cr - l Mo weld metal having low level of impurities and exhibiting excellent toughness up to minus o 18 C. Weld metal retains its mechanical properties even after prolonged heat treatments. The weld metal displays excellent creep resistance with controlled hardness. Ideal for welding steels of similar composition to achieve tough weld metals.
Element | C | Mn | Si | P | S | Cr | Mo | P+Sn |
Percent | 0.040 | 0.70 | 0.30 | 0.010 | 0.007 | 2.25 | 1.10 | 0.016 |
(PWHT: 690 C FOR 1 HR)
UTS | YS | Elongation | CVN Impact at minus |
(MPa) | (MPa) | (L= 4d)% | 18 C (Joules) |
630 | 530 | 24.0 | 100 |
Size (mm) | 6.3x450 | 5x450 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 260-320 | 180-240 | 140-180 | 100-130 | 70-100 |
Qty. (Pcs./Carton) | 25 | 35 | 55 | 75 | 100 |
E8018-B8
E8018-B3L
E8018-B1
E8018-B6
E8018-B8L
E9015-B24
E9018-G
E7018-B2L
E8018-D3
E8018-B8
E8018-G
E8018-D3
E9015-B23
E7018-A1
E9018-B3
E8018-B8L
E9018-B3
E9015-B3
E7018-B2L
E8018-B2 H4R
E7018-A1
E8018-B8
E8018-B2
E9015-B91
E7018-A1 H4R
E8018-B6
E9018-B91
E8018-B2
E9018-D1
E9018-G
E8015-B6
E9015-B92
E9016-B3
E8018-B2
E9018-B3
E8018-B6L
E9015-B92