Cromotherme-92 H4R is moisture resistant hydrogen controlled basic coated non synthetic electrode deposits 9Cr - 1Mo and enriched with Niobium, Vanadium, Nitrogen and Tungsten. Tungsten additions provides adequate creep rupture strength at higher steam pressures and temperatures. The controlled addition of alloying elements improves the toughness and weldability. It is designed to weld advanced materials, which are being used to improve thermal efficiency in power plant, refineries etc. Ideal for welding steels of similar composition to achieve adequate creep rupture strength. Some typical materials that are welded with this consumable are A213 T92, A335 P92, A387 Gr92, etc.
Element | C | Mn | Si | S | P | Cr | Ni | Mo | W | V | Nb | B | Al | Cu | N |
Percent | 0.10 | 0.70 | 0.25 | 0.007 | 0.012 | 9.0 | 0.60 | 0.50 | 1.70 | 0.20 | 0.06 | 0.002 | 0.02 | 0.10 | 0.05 |
(PWHT : 760°C FOR 1 HR)
UTS | YS | Elongation | Hardness |
(MPa) | (MPa) | (L= 4d)% | (BHW) |
690 | 580 | 19 | 225 |
DIFFUSIBLE HYDROGEN CONTENT: 4 ml / 100 gms of weld metal Max
MOISTURE AS CONDITIONED: 0.15 Max
MOISTURE AS EXPOSED (80% RH, 27 C FOR 9 HRS): 0.40 MAX
ADVANTAGE: Electrodes are Vacuum packed, no need of drying and can be used straight on the job.
Size (mm) | 5x350 | 4x350 | 3.15x350 | 2.15x350 |
Current Range (Amps) | 160-220 | 120-160 | 90-120 | 70-100 |
Qty. (Kgs./Carton) | 2 | 2 | 2 | 2 |
E8018-B8
E8018-B3L
E8018-B1
E8018-B6
E8018-B8L
E9015-B24
E9018-G
E7018-B2L
E8018-D3
E8018-B8
E8018-G
E8018-D3
E9015-B23
E7018-A1
E9018-B3
E8018-B3L
E8018-B8L
E9018-B3
E9015-B3
E7018-B2L
E8018-B2 H4R
E7018-A1
E8018-B8
E8018-B2
E9015-B91
E7018-A1 H4R
E8018-B6
E9018-B91
E8018-B2
E9018-D1
E9018-G
E8015-B6
E9016-B3
E8018-B2
E9018-B3
E8018-B6L
E9015-B92