•Non-synthetic electrode depositing low carbon 28Cr-31.5Ni-3.7Mo-1Cu, fully austenitic weld metal. • Weld metal exhibits excellent resistance to corrosion in non- oxidizing media like Sulfuric acid, Phosphoric acid, etc. • The elements C, P and S are maintained at low levels to eliminate hot cracking & fissuring problems in weld metal. • A soft and smooth arc, which is easy to strike and re-strike. • E a s y slag detachability and well-rippled weld beads. • The weld metal is of radiographic quality.
Ideally suited for welding stainless steels of similar composition and other equivalent grades of stainless steels.
Element | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
Percent | 0.025 | 1.5 | 0.90 | 27.7 | 31.5 | 3.7 | 0.010 | 0.005 | 1.0 |
UTS | Elongation |
(MPa) | (L= 5d)% |
574 | 35.0 |
Size (mm) | 5x350 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 150-180 | 110-140 | 80-100 | 60-80 |
Weight / Carton (kgs) | 2.5 | 2.5 | 2.5 | 2.5 |
E308L-16
E312-16
E316L-15 (Modified)
E2209-16
E310-16
E630-16
E2553-16
E308H-16
E318-16
E307-16(Nearest)
E309L-16
E410NiMo-16
E316-16
E316L-16
E316L-16
E316L-16
E316LMn-15
E410-26
E16-8-2-15
E308L-15
E309L-16
E308-16
E320-16
E309Nb-16
E316L-16
E316L-16 (Modified)
E307-15(Nearest)
E317L-16
E316L-16 (Nearest)
E308L-16 (Nearest)
E320LR-16
E33-31-16
E240-16
E347-16
E308L-16
E330H-15
E309-16
E385-16
E430-26
E347-15
E318L-16
E308L-16
E430-15
E316H-16
E410-15
E309Mo-16
E310MO-16
E2594-16
E2595-16
E16-8-2-16
E308H-17
E309LMo-17