Batox-16/8/2 is a basic coated, stainless steel electrode depositing 15.5Cr – 8.5Ni – 1.3Mo stainless steel weld metal. Electrodes provide excellent operating characteristics with easy slag detachability. The lean composition of weld metal minimize the in-service formation of inter-metallic compound, excellent hot ductility properties which offer freedom from weld or crater cracking even under high-restraint conditions. This lean version weld metal is ideally suited for welding stainless steels, such as types 16-8-2, 304H, 316H and 347H for high pressure, high temperature piping systems, and catalytic cracker structures.
FERRITE (AS WELDED): 5.0 Max. As Per WRC 1992
Element | C | Mn | Si | S | P | Cr | Ni | Mo |
Percent | 0.05 | 1.20 | 0.52 | 0.015 | 0.020 | 15.5 | 8.5 | 1.3 |
UTS | Elongation |
(MPa) | (L= 4d)% |
600 | 38.0 |
Size (mm) | 5x350 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 150-180 | 110-140 | 80-100 | 60-80 |
Quantity (Carton/kgs) | 2.5 | 2.5 | 2.5 | 2.5 |
E308L-16
E312-16
E316L-15 (Modified)
E2209-16
E310-16
E630-16
E2553-16
E308H-16
E318-16
E307-16(Nearest)
E309L-16
E410NiMo-16
E316-16
E316L-16
E316L-16
E316L-16
E316LMn-15
E410-26
E308L-15
E309L-16
E308-16
E320-16
E309Nb-16
E316L-16
E316L-16 (Modified)
E307-15(Nearest)
E317L-16
E316L-16 (Nearest)
E308L-16 (Nearest)
E320LR-16
E33-31-16
E240-16
E347-16
E308L-16
E330H-15
E309-16
E385-16
E430-26
E347-15
E318L-16
E308L-16
E430-15
E316H-16
E410-15
E309Mo-16
E310MO-16
E383-16
E2594-16
E2595-16
E16-8-2-16
E308H-17
E309LMo-17