A non-synthetic Inconel type of electrode, depositing weld metal of Ni-Cr-Co-Mo alloy. The weld metal has excellent crack resistance. Electrodes are used for welding similar type of alloys to themselves and to steel and for surfacing steels with Ni-Cr-Co-Mo weld metal. The electrodes are also used for applications where optimum strength and oxidation resistance is required above 820 deg C & up to 1150 deg C, especially when welding on base metal of Nickel-Iron-Chromium alloys. Specially recommended for welding furnace heating elements, reformer tubes etc.
Element | C | Mn | Fe | Si | Ni | Co | Cr | Nb+Ta | Mo |
Percent | 0.07 | 1.5 | 4.5 | 0.50 | 48.0 | 12.0 | 24.0 | 0.3 | 9.0 |
UTS | Elongation |
(MPa) | (L= 4d)% |
665 | 29 |
Size (mm) Dia x Length | 5x350 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 150-180 | 120-150 | 80-110 | 60-70 |
Weight/Carton (kgs) | 2.5 | 2.5 | 2.5 | 2.5 |
E310-15
ENiCrFe-3
ENiCrFe-7
ENi-1
ENiCrMo-3
ENiCrMo-7
ENiCrFe-9
ENiCrMo-12
ENiCu-7
ENiCrMo-4
ENiCrMo-5
ENiCrMo-14
ENiCrMo-10
ENiCrFe-2
ENiCrFe-3 (Approx.)
ENiCrFe-9
ENiCrMo-13
ENiMo-9
ENiCrMo-6
ENiCrFe-3